Preparation and Crystal Structure Characteristics of Starch-Ligand Complex
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以B-型微晶淀粉为原料,经二甲亚砜溶解后,分散到热水中,随后加入一定比例的硬脂酸、单硬脂酸甘油脂、棕榈酸和异戊醇的乙醇溶液中,再经过混合、结晶、离心分离、洗涤,制得淀粉-配体复合物。采用X-射线衍射仪对得到的复合物进行分析和测试,结果发现在单硬脂酸甘油脂∶淀粉质量比为1∶4的和硬脂酸∶淀粉质量比为1∶5的条件下制备的V-型复合物的晶型结构最优。

    Abstract:

    In the study,B-type microcrystal starch was firstly dissolved in DMSO and dispersed in the hot water,and then mixed with a certain proportion of the stearic acid,monostearin,palmitic acid and isoamyl alcohol,through crystallizing,centrifuging washing and formation of starch-ligand complex were acquired.X-ray diffractometer were used to analyze those complexes.the crystal structure of V-type complex was achieved at the ratio of monostearin to starch and stearic acid to starch is 1∶4 and 1∶5,respectively.

    参考文献
    相似文献
    引证文献
引用本文

刘延奇,秦令祥,王晓静.淀粉-配体复合物的制备及结晶结构研究[J].食品与生物技术学报,2010,29(4):488-490.

LIU Yan-qi, QIN Ling-xiang, WANG Xiao-jing. Preparation and Crystal Structure Characteristics of Starch-Ligand Complex[J]. Journal of Food Science and Biotechnology,2010,29(4):488-490.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2014-06-17
  • 出版日期:
文章二维码

版权所有:《食品与生物技术学报》编辑部

地址:江苏省无锡市蠡湖大道1800号  邮政编码:214122

电话:0510-85913526  电子邮件:xbbjb@jiangnan.edu.cn

技术支持:北京勤云科技发展有限公司

微信公众号二维码

手机版网站二维码