    摘要:

    研究了获得Ni-Co-Mo复合镀层的最佳工艺条件及该镀层的析氢催化活性。依此最佳工艺条件制得Ni-Co-Mo复合电极,其析氢超电势η100为112.8mV,比不加Mo粉制得的Ni-Co合金电极(η100=204.8mV)低92mV.比纯镍片(η100=453mV)低340.2mV.

    Abstract:

    The characteristics of hydrogen evolution of the Ni Co Mo cladding which was produced under designed technology conditions have been studied in laboratory. The factors affecting the formation of the cladding was investigated and the experimental result

    参考文献
    相似文献
    引证文献
引用本文

刘松琴,郑秋容,张景尧,张革新. Ni-Co-Mo镀层的析氢性能研究[J].食品与生物技术学报,1998,17(4).

Liu Songqin Zheng Qiurong Zhang Jingyao Zhang Gexin. Hydrogen Evolution of Reactivity Co deposited Ni Co Mo Electrodes[J]. Journal of Food Science and Biotechnology,1998,17(4).

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期:

版权所有:《食品与生物技术学报》编辑部

地址:江苏省无锡市蠡湖大道1800号  邮政编码:214122

电话:0510-85913526  电子邮件:xbbjb@jiangnan.edu.cn

技术支持:北京勤云科技发展有限公司

微信公众号二维码

手机版网站二维码