    摘要:

    采用原位接枝共聚法合成了改性淀粉/聚乳酸接枝共聚物。考察了3种改性剂对淀粉改性处理结果,探讨了改性淀粉接枝聚乳酸的共聚反应机理,用凝胶渗透色谱-多角度激光光散射联用仪(SEC/MALLS)、红外光谱仪(IR)和差示扫描量热仪(DSC)对共聚物结构进行表征,测试了共聚物的降解性能。结果表明,马来酸酐的改性效果最好,并成功合成了改性淀粉接枝聚乳酸共聚物,SEC/MALLS测得共聚物的相对分子质量Mw为6.921×104,Mn为4.789×104,相对分子质量分布Mw/Mn为1.445。降解实验结果为,在PBS中淀粉/聚乳酸共聚物降解速率较聚乳酸更快。

    Abstract:

    In this study,a modified starch-g-polylactic acid was synthesized by in situ graft copolymerization.Three modifiers were analyzed in modifying soluble starch,and the copolymerization mechanism was discussed preliminarily.The copolymer was characterized by IR,(H1-NMR) and SEC/MALLS.It is concluded that maleic anhydride was the best modifier,contributing to starch grafting with PLA;molecular weight(Mw)of the copolymer is to be 6.921×104,molecular weight distribution(Mw/Mn) 1.445.In addition,the degradation study showed that mass of the copolymer degraded faster than that of PLA in PBS buffer solution.

    参考文献
    相似文献
    引证文献
引用本文

杨小玲,王珊.改性淀粉/聚乳酸共聚物的生物降解性研究[J].食品与生物技术学报,2010,29(2):197-200.

YANG Xiao-ling, WANG Shan. The Biodegradability of Modified Starch Grafting Polylactic Acid[J]. Journal of Food Science and Biotechnology,2010,29(2):197-200.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2014-06-17
  • 出版日期:

版权所有:《食品与生物技术学报》编辑部

地址:江苏省无锡市蠡湖大道1800号  邮政编码:214122

电话:0510-85913526  电子邮件:xbbjb@jiangnan.edu.cn

技术支持:北京勤云科技发展有限公司

微信公众号二维码

手机版网站二维码