刺槐豆多糖纳米硒的制备及表征
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

基金项目:


Preparation and Characterization of Nano-Selenium with Locust Bean Polysaccharides as Soft Template
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以刺槐豆多糖为软模板,用抗坏血酸还原亚硒酸法制备纳米硒,探讨反应时间、温度、刺槐豆多糖及抗坏血酸浓度对产物粒径和形貌的影响,并采用紫外光谱(UV)、X衍射和扫描电镜(SEM)进行表征。结果表明:当抗坏血酸和亚硒酸摩尔比为5∶1,刺槐豆多糖质量分数为0.2‰,60 ℃反应4 h后可得红色均匀的球状纳米硒颗粒,平均粒径为95~100 nm。

    Abstract:

    Nano-selenium was prepared with locust bean polysaccharides as soft template by the reduction of ascorbic acid(Vc) to selenious acid and characterized by UV and SEM. The effects of reaction time, temperature, locust bean polysaccharide and Vc concentration on particle size and morphology of the resulting product were investigated. The results showed that uniformly red globular nano-selenium was obtained with average diameter about 95~100 nm when the mass fraction of locust bean polysaccharide was 0.2‰ and the molar ratio of ascorbic acid to selenite 5∶1 at 60 ℃ for 4 h.

    参考文献
    相似文献
    引证文献
引用本文

高义霞,周向军,袁毅君,鲜鹏杰.刺槐豆多糖纳米硒的制备及表征[J].食品与生物技术学报,2014,33(9):997-1002.

GAO Yixia, ZHOU Xiangjun, YUAN Yijun, XIAN Pengjie. Preparation and Characterization of Nano-Selenium with Locust Bean Polysaccharides as Soft Template[J]. Journal of Food Science and Biotechnology,2014,33(9):997-1002.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2014-10-19
  • 出版日期:

版权所有:《食品与生物技术学报》编辑部

地址:江苏省无锡市蠡湖大道1800号  邮政编码:214122

电话:0510-85913526  电子邮件:xbbjb@jiangnan.edu.cn

技术支持:北京勤云科技发展有限公司

微信公众号二维码

手机版网站二维码