Preparation of Thiohydroxy Modified Magnetic Mesoporous Silica from Rice Husk and its Removal Properties for Cd （II）
Author:
Affiliation:

Fund Project:

  • 摘要
    • |
  • 图/表
    • |
  • 访问统计
    • |
  • 参考文献
    • |
  • 相似文献
    • |
  • 引证文献
    • |
  • 资源附件
    • |
  • 文章评论
    摘要:

    以稻壳灰为硅源、Fe3O4为磁性材料制备磁性介孔二氧化硅（MMS）；随后对其进行巯基改性制备巯基改性磁性介孔二氧化硅（TMMS），并考察了搅拌时间、反应温度、氨水添加量对TMMS表面巯基浓度的影响，研究了巯基浓度对Cd2+吸附效果的影响；最后，对MMS与TMMS的结构进行表征，并通过吸附等温线对MMS与TMMS对Cd2+吸附效果进行比较。结果表明：当反应时间8 h、水浴温度80 ℃、催化剂氨水添加量750 ?滋L时，TMMS的表面巯基浓度达到0.131 mmol/g；巯基浓度越高，TMMS对Cd2+的吸附效果越好；MMS与TMMS两种材料的骨架均为无定形的SiO2结构，BET多点比表面积分别为581.769 m2/g与405.665 m2/g；MMS与TMMS对Cd2+的等吸附温模型更符合Langmuir模型，都属于单分子层吸附；在Langmuir模型中，TMMS的饱和吸附量为33.33 mg/g，大于MMS的饱和吸附量（21.50 mg/g）。因此，巯基改性有利于TMMS对Cd2+的吸附，可达到有效脱除废水中Cd2+的目的。

    Abstract:

    In this paper，magnetic mesoporous silica （MMS） was prepared by using rice husk ash as the silica source and Fe3O4 as the magnetic material，and then MMS was modified by TMMPS as the silane coupling agents. The effects of agitation time，reaction temperature and the amount of ammonia on the surface thiohydroxy concentration were investigated during the preparation process and the effect of surface thiohydroxy concentration on the adsorption capacity on Cd2+ was investigated during the adsorption process. At last，the end product named thiohydroxy modified magnetic mesoporous silica （TMMS） and MMS was characterized and the adsorption effect of MMS and TMMS for Cd2+ was compared by adsorption isotherm. It was found that when the reaction condition was 8 h at 80 ℃ and the amount of ammonia was 750 ?滋L，the surface thiohydroxy concentration of TMMS was 0.131 mmol/g. The adsorption effect was in direct proportion to the surface thiohydroxy concentration. The BET surface area of MMS and TMMS was 581.769 m2/g and 405.665 m2/g respectively. The isotherm had a good correlation with Langmuir isotherm model rather than Freundlich isotherm model，which suggesting that the adsorption was monolayer adsorption. When the reaction temperature during the adsorption process was 30 ℃，the saturated adsorption capacity of TMMS was 33.33 mg/g，which was bigger than the value of MMS. Therefore，the purpose of effective removal of Cd2+ in wastewater can be achieved by modification.

    参考文献
    相似文献
    引证文献
引用本文

周丽枫,王韧,冯伟,李亚男,周蕴宇,罗小虎,王莉,于秋生,陈正行.巯基改性磁性介孔二氧化硅的制备及其对重金属Cd2+的吸附研究[J].食品与生物技术学报,2018,37(10):1035-1041.

ZHOU Lifeng, WANG Ren, FENG Wei, LI Yanan, ZHOU Yunyu, LUO Xiaohu, WANG Li, YU Qiusheng, CHEN Zhengxing. Preparation of Thiohydroxy Modified Magnetic Mesoporous Silica from Rice Husk and its Removal Properties for Cd （II）[J]. Journal of Food Science and Biotechnology,2018,37(10):1035-1041.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2018-11-14
  • 出版日期:

版权所有：《食品与生物技术学报》编辑部

地址：江苏省无锡市蠡湖大道1800号  邮政编码：214122

电话：0510-85913526  电子邮件：xbbjb@jiangnan.edu.cn

技术支持：北京勤云科技发展有限公司

微信公众号二维码

手机版网站二维码